Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL GTX™ Resin GTX951W - Europe - (PPE+PA*) - Saudi Basic Industries Corporation (SABIC)

Check here, which other Noryl GTX datasheets, application examples or technical articles are available in Material Data Center

Processing/Physical Characteristics - 機械的特性 - 熱的特性 - 電気的特性. - その他の特性. - Processing Recommendation Injection Molding - 機能

Any use of this information falls under the rules of our disclaimer.

商品の説明文

NORYL GTX™ 951W resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high heat resistance, excellent chemical resistance, high melt flow, and added mold release. NORYL GTX951W resin was designed for automotive under-the-hood applications such as power distribution boxes, relay boxes, and junction boxes.

Processing/Physical Characteristics	値	単位	テスト基準
ISO データ
溶融時の密度	955	kg/m³	-
溶融時の熱伝導率	0.2	W/(m K)	-
溶融時の比熱	1500	J/(kg K)	-
突き出し時の時の温度	216	°C	-
ASTM数据
メルトフローレイト, MFI	65	g/10min	ASTM D 1238
温度	280	°C	-
荷重	5	kg	-
成形収縮率., 平行	1.55	mm/mm	ASTM D 955
成形収縮率, 直角	1.35	mm/mm	ASTM D 955

機械的特性	値	単位	テスト基準
ISO データ
引張弾性率	2500	MPa	ISO 527
降伏応力	66	MPa	ISO 527
破壊ひずみ	50	%	ISO 527
曲げ弾性率	2370	MPa	ISO 178
ASTM数据
引張弾性率	2250	MPa	ASTM D 638
降伏応力	65	MPa	ASTM D 638
破壊応力	57	MPa	ASTM D 638
降伏点伸び	5	%	ASTM D 638
破断伸び	55	%	ASTM D 638
ノッチ付きIzod衝撃強さ, 1/8 in	211	J/m	ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature	100	J/m	ASTM D 256
温度	-30	°C	-

熱的特性	値	単位	テスト基準
ISO データ
線膨張係数, 平行	100	E-6/K	ISO 11359-1/-2
線膨張係数, 直角	100	E-6/K	ISO 11359-1/-2

電気的特性.	値	単位	テスト基準
ASTM数据
耐電圧, 短い時間	22.4	kV/mm	ASTM D 149
誘電正接, 1 MHz	0.017	-	ASTM D 150

その他の特性.	値	単位	テスト基準
密度.	1110	kg/m³	ISO 1183
密度	1100	kg/m³	ASTM D 792

Processing Recommendation Injection Molding	値	単位	テスト基準
Pre-drying - Temperature	95 - 105	°C	-
Pre-drying - Time	3 - 4	h	-
Processing humidity	≤0.07	%	-
樹脂温度	270 - 295	°C	-
金型温度	65 - 95	°C	-
Zone 1	255 - 295	°C	-
Zone 2	260 - 295	°C	-
Zone 3	265 - 295	°C	-
Screw speed	20 - 100	rpm	-
Back pressure	0.3 - 1.4	MPa	-

機能

特殊な特性

成形加工法.

射出成形.

アプリケーション

自動車

領域別の利用可能性

ヨーロッパ.

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com

Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.